- AWS A5.28: E110C-K4
- AS/NZS 18276 B-T765T15-0MA-N4C1M2-U H5
Typical All Weld Metal Chemical Analysis |
|
|
|
|
|
|
Shielding Gas |
C |
Mn |
Si |
S |
P |
Ni |
Cr |
Mo |
75% Ar/ 25% CO2 |
0.07 |
1.52 |
0.52 |
0.007 |
0.004 |
1.92 |
0.18 |
0.47 |
90% Ar/ 10% CO2 |
0.08 |
1.50 |
0.50 |
0.005 |
0.003 |
1.84 |
0.24 |
0.46 |
Typical Diffusible Hydrogen |
|
Hydrogen Equipment |
75% Ar/25% CO2 |
90% Ar/ 10% CO2 |
Gas Chromatography |
1.5ml /100g |
1.6ml /100g |
Typical All Weld Metal Mechanical Analysis (As Welded) |
|
Gas Type |
75% Ar/25% CO2 |
90% Ar/ 10% CO2 |
Tensile Strength |
810 MPa |
883 MPa |
Yield Strength |
725 MPa |
800 MPa |
Elongation |
19% |
17% |
CVN Impact Values |
28J @ -50ºC |
38J @ -50ºC |
FabCOR-1100_Spec-Sheet_052017_FINAL.pdf (welding.com.au)